+86 13075358901
WhatsApp| Place of Origin: | Shandong |
| Brand Name: | Hanwu |
| Certification: | ISO ,BV ,SGS, CE |
| Minimum Order Quantity: | 1 tons |
| Packaging Details: | water proof paper is inner packing, galvanized steel or coated steel sheet is outer packing , side guard plate , then wrapped by seven steel belt. |
| Delivery Time: | 15-20 days or subject to the clients' requirement and quantity |
| Payment Terms: | 30%TT for deposit, 70% balance before shipment or LC at sight |
| Supply Ability: | 20000 tons per month |
316L stainless steel bar just has a lower carbon content than 316 stainless steel bar and it is used mostly for welding purposes. The lower carbon content greatly lowers the precipitation of carbides in the heat-affected zone close to the weld, and such precipitation is likely to lead to intergranular corrosion of stainless steel in certain settings. Basically, their is no need to anneal weld joints prior to using the completed metal form using 304L, which helps save time and effort. 316L stainless steel bar is one of the most widely used stainless steel bars like 304, with better corrosion resistance. 316L stainless steel bar also has high temperature resistance that can go with up to 1000 degrees. Lastly, 316L stainless steel has stronger rust resistance than 200 series stainless steel materials.
| Product Name | 316L Stainless Steel Bar | |
| Type | Steel Bar | |
| Outer Diameter | Round Bar | 4mm-500mm |
| Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
| Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
| Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
| Length | 1-6 meters, Length can be customized | |
| Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
| Surface | Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. | |
| Scope of Application | Stainless steel bars are used in a variety of industries such as shipbuilding,Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement,Heavy earthmoving equipment and construction, etc. | |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P | Mo |
| ≤ 0.03 | ≤1.0 | ≤ 2.0 | 16.0～18.0 | 10.0～14.0 | ≤ 0.03 | ≤ 0.045 | 2.0～3.0 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥480 | ≥177 | ≥ 40 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
| 7.99 | 193 | 16.0 | 16.2 | 74 |